Efecto de la velocidad de avance y corriente de trabajo en la calidad de las soldaduras producidas por flux cored con electrodo tubular

Simple item page
dc.contributor.advisorJimenez Forero, Hernando Augustospa
dc.contributor.authorPiracoca Balaguera, Julieth Andreaspa
dc.contributor.authorDiaz Torres, Jeison Felipespa
dc.date.accessioned2021-03-02T16:39:52Z
dc.date.available2021-03-02T16:39:52Z
dc.date.issued2020-07-21spa
dc.description.abstractIn this project, an analysis of the effect of the application parameters (forward speed and current), on the quality, mechanical properties and composition of the gas-protected tubular electrode weld, applied by the flux cored process, on pieces of A572 steel. The development of the project will be presented in 4 methodological phases that cover the theoretical analysis and the state of the art of the flux cored process, passing through the stage of test tube preparation, characterization of the same, until culminating in the writing of reports that condense the results obtained. The quality of the weld will be evaluated using non-destructive techniques such as visual inspection, penetrating liquids, magnetic particles and ultrasound, while mechanical tests such as stress and microhardness tests will be carried out in order to determine the integrity of the applied weld at different current conditions and forward speed. As a result of the tests carried out on the quality of the weld, taking into account the working conditions such as current, it can be indicated that when using the highest value, the properties of the steel were found to be more favorable, revealing that the material it behaves in a more fragile way and achieves a greater measure of hardness, taking into account that in the elastic zone of the material, no significant deformations are generated when applying great forces. For the different conditions of advance speed, it can be highlighted that by applying the weld faster, better conditions were obtained during the tests, showing, for example, an average increase of 50% in resistance to elastic deformation.eng
dc.description.abstractEn este proyecto se realizara un anĆ”lisis del efecto de los parĆ”metros de aplicaciĆ³n (velocidad de avance y corriente), en la calidad, propiedades mecĆ”nicas y composiciĆ³n de la soldadura de electrodo tubular con protecciĆ³n gaseosa, aplicadas mediante el proceso flux cored, sobre piezas de acero A572. El desarrollo del proyecto se presentara en 4 fases metodolĆ³gicas que abarcan el anĆ”lisis teĆ³rico y el estado del arte del proceso de flux cored, pasando por la etapa de preparaciĆ³n de probetas, caracterizaciĆ³n de las mismas, hasta culminar con la redacciĆ³n de reportes que condensen los resultados obtenidos. La calidad de la soldadura va a ser evaluada mediante las tĆ©cnicas no destructivas como inspecciĆ³n visual, lĆ­quidos penetrantes, partĆ­culas magnĆ©ticas y ultrasonido, a su vez se realizaran pruebas mecĆ”nicas como ensayo de tensiĆ³n y microdureza con el fin de determinar la integridad de la soldadura aplicada a diferentes condiciones de corriente y velocidad de avance. Como resultado de las pruebas realizadas a la calidad de la soldadura, teniendo en cuenta las condiciones de trabajo como la corriente, se puede indicar que al emplear el valor mĆ”s alto, se encontrĆ³ que las propiedades del acero fueron mĆ”s favorables, revelando que el material se comporta de manera mĆ”s frĆ”gil y alcanza una mayor medida de dureza, teniendo en cuenta que en la zona elĆ”stica del material, no se generan deformaciones significativas al aplicar grandes esfuerzos. Para las distintas condiciones de velocidad de avance, se puede resaltar que al aplicar la soldadura de manera mĆ”s rĆ”pida, se obtuvieron mejores condiciones durante las pruebas, mostrando por ejemplo un incremento promedio del 50%, en la resistencia a la deformaciĆ³n elĆ”stica.spa
dc.description.degreelevelPregradospa
dc.description.degreenameIngeniero(a) ElectromecƔnico(a)spa
dc.description.degreenameIngeniero(a) MecƔnico(a)spa
dc.description.funderCosto total del proyecto $ 4,585,000.00. FinanciaciĆ³n propia $ 750,000.00. FinanciaciĆ³n UAN $ 1,090,000.00. FinanciaciĆ³n externa $ 2,745,000.00.es_ES
dc.description.notesPresencialspa
dc.description.sponsorshipOtrospa
dc.identifier.bibliographicCitationESAB. (2019). CENTRO DE CONOCIMIENTO ESAB. Obtenido de Proceso de Soldadura FCAW: Obtenido de https://www.esab.com.ar/ar/sp/education/blog/proceso-soldadura-fcaw-alambre-tubular-relleno-de-fundente-definiciones-del-proceso.cfmspa
dc.identifier.bibliographicCitationMetalurgia. (Septiembre de 2007). Blogspot. Obtenido de http://metalurgia-metalurgia.blogspot.com/2007/09/soldadura-por-arco-con-ncleo-de.htmlspa
dc.identifier.bibliographicCitationHerrera, I. A. (2016). Soldadura y Estructuras. Recuperado el 5 de Marzo de 2019, de http://soldadurayestructuras.com/proceso-fcaw.htmlspa
dc.identifier.bibliographicCitationPacheco, J. D. (2014). ESTUDIO COMPARATIVO DE ALAMBRES TUBULARES METAL CORED Y TUBULARES FLUX CORED EN PROCESOS DE SOLDADURA SEMIAUTOMƁTICOS. BogotƔ. Recuperado el 3 de Marzo de 2019spa
dc.identifier.bibliographicCitationSoldexa. (2019). ESAB. Recuperado el 15 de Octubre de 2019 de https://www.soldexa.com.pe/soldexa/sp/index.cfmspa
dc.identifier.bibliographicCitationCano, H. B. (2019). SupervisiĆ³n de Estructuras de Concreto y de Acero. Recuperado el 6 de Marzo de 2019, de https://sites.google.com/site/construyetuingenio2013/5-procesos-de-soldadura-y-corte/5-4-soldadura-por-arco-con-nucleo-de-fundente-fcawspa
dc.identifier.bibliographicCitationAmerican Welding Society. (2015). Specification for Carbon Steel Electrodes for Flux Cored Arc Welding. United States of America: American Welding Society. Recuperado el 5 de Marzo de 2019spa
dc.identifier.bibliographicCitationMoreno, Carlos. Soldadura y robĆ³tica. (2012). Gases de protecciĆ³n para soldadura MIG- MAG-GMAW. Recuperado el 20 de Mayo de 2020 de https://www.josecarlosmoreno.com/copia-de-mig-mag-gmaw-tipos-de-arcospa
dc.identifier.bibliographicCitationRibas JosĆ©. (2010). TĆ©cnicas de soldadura y gases de protecciĆ³n. Recuperado el 10 de Abril de 2020 de https://dissenyproducte.blogspot.com/2016/05/tecnicas-de-soldadura-y-gases-de.htmlspa
dc.identifier.bibliographicCitationASTM A572-GR50. (8 de Mayo de 2018). Standard Specification for High-Strength Low-Alloy Columbium-Vanadium Structural. A572/A572M. Recuperado el 10 de Marzo de 2019spa
dc.identifier.bibliographicCitationCanelo, Carlos. Ensayo a tracciĆ³n del acero 1045. Recuperado el 10 de Junio 2020 dehttps://www.researchgate.net/publication/331310934_Ensayo_a_traccion_de_acero_1045spa
dc.identifier.bibliographicCitationGarcĆ­a Romero, introducciĆ³n a la ciencia de los materiales y sus propiedades (l). 2018. Universidad de PaĆ­s Vasco. Recuperado el 5 de Junio de 2020, de https://ocw.ehu.eus/pluginfile.php/17292/mod_resource/content/0/Tema%207Rotura%20y%20fallo%20mec%C3%A1nico%20de%20los%20materiales.pdfspa
dc.identifier.bibliographicCitationEnsayo de microdureza. Recuperado el 10 de mayo de 2020 de https://matensayos.webcindario.com/ensayos/microdurezas.htmspa
dc.identifier.bibliographicCitationFRADE, RubƩn. Propiedades fƭsico-mecƔnicas de los materiales. Recuperado el 20 de noviembre de 2019 de fradeblogs.wordpress.com/2013/11/21/propiedades-fisico-mecanicas-de-los-materiales/.spa
dc.identifier.bibliographicCitationMetfusion. (2013) Discontinuidades internas. Recuperado el 20 de Mayo de 2020 de https://metfusion.wordpress.com/2013/08/10/imperfecciones-en-soldadura-tipos-de-discontinuidades/.spa
dc.identifier.bibliographicCitationAEND. Ensayos no destructivos partĆ­culas magnĆ©ticas. FundaciĆ³n Confametal. Recuperado el 25 de Mayo de 2020spa
dc.identifier.bibliographicCitationBarrera, Lizeth. (2011). Desarrollo y procedimientos para la utilizaciĆ³n de tĆ©cnicas de ensayos no destructivos con ultrasonido para la inspecciĆ³n de tuberĆ­as. Universidad Pontificia Bolivariana. Recuperado el 20 de Mayo de 2020 de http://biblioteca.upbbga.edu.co/docs/digital_21062.pdfspa
dc.identifier.bibliographicCitationTextos cientĆ­ficos. (2020). El acero. Recuperado el 30 de abril de 2020 de https://www.textoscientificos.com/quimica/acerospa
dc.identifier.bibliographicCitationHernĆ”ndez, Yodi. (2018). Estudio de la soldabilidad del acero estructural ASTM A572 grado 50 con proceso SMAW. Universidad PedagĆ³gica y tecnolĆ³gica de Colombia. Recuperado el 10 de Mayo de 2020 de https://repositorio.uptc.edu.co/bitstream/001/3046/1/TGT_1630.pdfspa
dc.identifier.bibliographicCitationAEISA. 2019. LĆ­quidos penetrantes. Recuperado el 10 de mayo de 2020 de https://www.aeisa.com.mx/liquidos-penetrantes-todo-lo-que-tienes-que-saber-sobre-esta-prueba-no-destructiva/spa
dc.identifier.bibliographicCitationMetfusion. 2013. Imperfecciones en la soldadura tipos de discontinuidades. Recuperado el 10 de mayo de 2020 de https://metfusion.wordpress.com/2013/08/10/imperfecciones-en-soldadura-tipos-de-discontinuidades/spa
dc.identifier.bibliographicCitationRomero Bernardo, Proboste Felipe. 2013. AplicaciĆ³n de ultrasonido al control de calidad de procedo de soldadura. Universidad del BIO BIO. Facultad de ingenierĆ­a, recuperado el 20 de mayo de 2020 de http://repobib.ubiobio.cl/jspui/bitstream/123456789/799/1/Romero_Reyes_Bernardo.pdfspa
dc.identifier.bibliographicCitationUniversidad TecnolĆ³gica de Pereira. MetalografĆ­a. (2020) Recuperado el 20 de mayo de 2020, de http://blog.utp.edu.co/metalografia/5-diagrama-hierro-carbono/spa
dc.identifier.bibliographicCitationDomĆ­nguez, Alonso. (2017) CaracterizaciĆ³n microestructural de un acero de bajo carbono y contenido de manganeso cercanos al 1.5%, templado a temperaturas intercrĆ­ticas y revenido. BogotĆ”. Recuperado el 30 de Mayo de 2020 de http://www.crystallography.net/cod/result.phpspa
dc.identifier.instnameinstname:Universidad Antonio NariƱospa
dc.identifier.reponamereponame:Repositorio Institucional UANspa
dc.identifier.repourlrepourl:https://repositorio.uan.edu.co/spa
dc.identifier.urihttp://repositorio.uan.edu.co/handle/123456789/2232
dc.language.isospaspa
dc.publisherUniversidad Antonio NariƱospa
dc.publisher.campusBogotĆ” - Surspa
dc.publisher.facultyFacultad de IngenierĆ­a MecĆ”nica, ElectrĆ³nica y BiomĆ©dicaspa
dc.publisher.programIngenierƭa ElectromecƔnicaspa
dc.publisher.programIngenierƭa MecƔnicaspa
dc.rightsAcceso abierto
dc.rights.accessrightsinfo:eu-repo/semantics/openAccessspa
dc.rights.coarhttp://purl.org/coar/access_right/c_abf2spa
dc.rights.licenseAttribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)spa
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/spa
dc.subjectCorrientees_ES
dc.subjectSoldaduraes_ES
dc.subjectFlux coredes_ES
dc.subjectElectrodo tubulares_ES
dc.subjectVelocidad de avancees_ES
dc.subject.keywordCurrentes_ES
dc.subject.keywordWeldinges_ES
dc.subject.keywordFlux coredes_ES
dc.subject.keywordTubular electrodees_ES
dc.subject.keywordForward speedes_ES
dc.titleEfecto de la velocidad de avance y corriente de trabajo en la calidad de las soldaduras producidas por flux cored con electrodo tubulares_ES
dc.typeTrabajo de grado (Pregrado y/o EspecializaciĆ³n)spa
dc.type.coarhttp://purl.org/coar/resource_type/c_7a1fspa
dc.type.coarversionhttp://purl.org/coar/version/c_970fb48d4fbd8a85
dc.type.versioninfo:eu-repo/semantics/acceptedVersionspa
Files
Original bundle
Now showing 1 - 2 of 2
thumbnail.default.alt
Name:
2020Julieth AndreaPiracoca Balaguera
Size:
2.96 MB
Format:
Adobe Portable Document Format
Description:
Trabajo de grado
Download
thumbnail.default.alt
Name:
2020AutoirzaciondeAutores.pdf
Size:
462.49 KB
Format:
Adobe Portable Document Format
Description:
AutorizaciĆ³n de autores
License bundle
Now showing 1 - 1 of 1
thumbnail.default.alt
Name:
license.txt
Size:
2.65 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Ingenierƭa electromecƔnica