Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)Jimenez Forero, Hernando AugustoPiracoca Balaguera, Julieth AndreaDiaz Torres, Jeison Felipe2021-03-022021-03-022020-07-21http://repositorio.uan.edu.co/handle/123456789/2232In this project, an analysis of the effect of the application parameters (forward speed and current), on the quality, mechanical properties and composition of the gas-protected tubular electrode weld, applied by the flux cored process, on pieces of A572 steel. The development of the project will be presented in 4 methodological phases that cover the theoretical analysis and the state of the art of the flux cored process, passing through the stage of test tube preparation, characterization of the same, until culminating in the writing of reports that condense the results obtained. The quality of the weld will be evaluated using non-destructive techniques such as visual inspection, penetrating liquids, magnetic particles and ultrasound, while mechanical tests such as stress and microhardness tests will be carried out in order to determine the integrity of the applied weld at different current conditions and forward speed. As a result of the tests carried out on the quality of the weld, taking into account the working conditions such as current, it can be indicated that when using the highest value, the properties of the steel were found to be more favorable, revealing that the material it behaves in a more fragile way and achieves a greater measure of hardness, taking into account that in the elastic zone of the material, no significant deformations are generated when applying great forces. For the different conditions of advance speed, it can be highlighted that by applying the weld faster, better conditions were obtained during the tests, showing, for example, an average increase of 50% in resistance to elastic deformation.En este proyecto se realizara un análisis del efecto de los parámetros de aplicación (velocidad de avance y corriente), en la calidad, propiedades mecánicas y composición de la soldadura de electrodo tubular con protección gaseosa, aplicadas mediante el proceso flux cored, sobre piezas de acero A572. El desarrollo del proyecto se presentara en 4 fases metodológicas que abarcan el análisis teórico y el estado del arte del proceso de flux cored, pasando por la etapa de preparación de probetas, caracterización de las mismas, hasta culminar con la redacción de reportes que condensen los resultados obtenidos. La calidad de la soldadura va a ser evaluada mediante las técnicas no destructivas como inspección visual, líquidos penetrantes, partículas magnéticas y ultrasonido, a su vez se realizaran pruebas mecánicas como ensayo de tensión y microdureza con el fin de determinar la integridad de la soldadura aplicada a diferentes condiciones de corriente y velocidad de avance. Como resultado de las pruebas realizadas a la calidad de la soldadura, teniendo en cuenta las condiciones de trabajo como la corriente, se puede indicar que al emplear el valor más alto, se encontró que las propiedades del acero fueron más favorables, revelando que el material se comporta de manera más frágil y alcanza una mayor medida de dureza, teniendo en cuenta que en la zona elástica del material, no se generan deformaciones significativas al aplicar grandes esfuerzos. Para las distintas condiciones de velocidad de avance, se puede resaltar que al aplicar la soldadura de manera más rápida, se obtuvieron mejores condiciones durante las pruebas, mostrando por ejemplo un incremento promedio del 50%, en la resistencia a la deformación elástica.spaAcceso abiertoCorrienteSoldaduraFlux coredElectrodo tubularVelocidad de avanceEfecto de la velocidad de avance y corriente de trabajo en la calidad de las soldaduras producidas por flux cored con electrodo tubularTrabajo de grado (Pregrado y/o Especialización)CurrentWeldingFlux coredTubular electrodeForward speedinfo:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2ESAB. (2019). CENTRO DE CONOCIMIENTO ESAB. Obtenido de Proceso de Soldadura FCAW: Obtenido de https://www.esab.com.ar/ar/sp/education/blog/proceso-soldadura-fcaw-alambre-tubular-relleno-de-fundente-definiciones-del-proceso.cfmMetalurgia. (Septiembre de 2007). Blogspot. Obtenido de http://metalurgia-metalurgia.blogspot.com/2007/09/soldadura-por-arco-con-ncleo-de.htmlHerrera, I. A. (2016). Soldadura y Estructuras. Recuperado el 5 de Marzo de 2019, de http://soldadurayestructuras.com/proceso-fcaw.htmlPacheco, J. D. (2014). ESTUDIO COMPARATIVO DE ALAMBRES TUBULARES METAL CORED Y TUBULARES FLUX CORED EN PROCESOS DE SOLDADURA SEMIAUTOMÁTICOS. Bogotá. Recuperado el 3 de Marzo de 2019Soldexa. (2019). ESAB. Recuperado el 15 de Octubre de 2019 de https://www.soldexa.com.pe/soldexa/sp/index.cfmCano, H. B. (2019). Supervisión de Estructuras de Concreto y de Acero. Recuperado el 6 de Marzo de 2019, de https://sites.google.com/site/construyetuingenio2013/5-procesos-de-soldadura-y-corte/5-4-soldadura-por-arco-con-nucleo-de-fundente-fcawAmerican Welding Society. (2015). Specification for Carbon Steel Electrodes for Flux Cored Arc Welding. United States of America: American Welding Society. Recuperado el 5 de Marzo de 2019Moreno, Carlos. Soldadura y robótica. (2012). Gases de protección para soldadura MIG- MAG-GMAW. Recuperado el 20 de Mayo de 2020 de https://www.josecarlosmoreno.com/copia-de-mig-mag-gmaw-tipos-de-arcoRibas José. (2010). Técnicas de soldadura y gases de protección. Recuperado el 10 de Abril de 2020 de https://dissenyproducte.blogspot.com/2016/05/tecnicas-de-soldadura-y-gases-de.htmlASTM A572-GR50. (8 de Mayo de 2018). Standard Specification for High-Strength Low-Alloy Columbium-Vanadium Structural. A572/A572M. Recuperado el 10 de Marzo de 2019Canelo, Carlos. Ensayo a tracción del acero 1045. Recuperado el 10 de Junio 2020 dehttps://www.researchgate.net/publication/331310934_Ensayo_a_traccion_de_acero_1045García Romero, introducción a la ciencia de los materiales y sus propiedades (l). 2018. Universidad de País Vasco. Recuperado el 5 de Junio de 2020, de https://ocw.ehu.eus/pluginfile.php/17292/mod_resource/content/0/Tema%207Rotura%20y%20fallo%20mec%C3%A1nico%20de%20los%20materiales.pdfEnsayo de microdureza. Recuperado el 10 de mayo de 2020 de https://matensayos.webcindario.com/ensayos/microdurezas.htmFRADE, Rubén. Propiedades físico-mecánicas de los materiales. Recuperado el 20 de noviembre de 2019 de fradeblogs.wordpress.com/2013/11/21/propiedades-fisico-mecanicas-de-los-materiales/.Metfusion. (2013) Discontinuidades internas. Recuperado el 20 de Mayo de 2020 de https://metfusion.wordpress.com/2013/08/10/imperfecciones-en-soldadura-tipos-de-discontinuidades/.AEND. Ensayos no destructivos partículas magnéticas. Fundación Confametal. Recuperado el 25 de Mayo de 2020Barrera, Lizeth. (2011). Desarrollo y procedimientos para la utilización de técnicas de ensayos no destructivos con ultrasonido para la inspección de tuberías. Universidad Pontificia Bolivariana. Recuperado el 20 de Mayo de 2020 de http://biblioteca.upbbga.edu.co/docs/digital_21062.pdfTextos científicos. (2020). El acero. Recuperado el 30 de abril de 2020 de https://www.textoscientificos.com/quimica/aceroHernández, Yodi. (2018). Estudio de la soldabilidad del acero estructural ASTM A572 grado 50 con proceso SMAW. Universidad Pedagógica y tecnológica de Colombia. Recuperado el 10 de Mayo de 2020 de https://repositorio.uptc.edu.co/bitstream/001/3046/1/TGT_1630.pdfAEISA. 2019. Líquidos penetrantes. Recuperado el 10 de mayo de 2020 de https://www.aeisa.com.mx/liquidos-penetrantes-todo-lo-que-tienes-que-saber-sobre-esta-prueba-no-destructiva/Metfusion. 2013. Imperfecciones en la soldadura tipos de discontinuidades. Recuperado el 10 de mayo de 2020 de https://metfusion.wordpress.com/2013/08/10/imperfecciones-en-soldadura-tipos-de-discontinuidades/Romero Bernardo, Proboste Felipe. 2013. Aplicación de ultrasonido al control de calidad de procedo de soldadura. Universidad del BIO BIO. Facultad de ingeniería, recuperado el 20 de mayo de 2020 de http://repobib.ubiobio.cl/jspui/bitstream/123456789/799/1/Romero_Reyes_Bernardo.pdfUniversidad Tecnológica de Pereira. Metalografía. (2020) Recuperado el 20 de mayo de 2020, de http://blog.utp.edu.co/metalografia/5-diagrama-hierro-carbono/Domínguez, Alonso. (2017) Caracterización microestructural de un acero de bajo carbono y contenido de manganeso cercanos al 1.5%, templado a temperaturas intercríticas y revenido. Bogotá. Recuperado el 30 de Mayo de 2020 de http://www.crystallography.net/cod/result.phpinstname:Universidad Antonio Nariñoreponame:Repositorio Institucional UANrepourl:https://repositorio.uan.edu.co/