Obtención y caracterización de un material compuesto de matriz poliéster reforzado con pulverizado de madera de café

Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)Solano Moreno, Martha LuciaQuintero Fajardo, Rafael Ricardo2022-10-082022-10-082022-05-30http://repositorio.uan.edu.co/handle/123456789/7058A biocomposite material was obtained and characterized from the polyester matrix and the reinforcement with pulverized coffee wood; motivated by a need to take advantage of the coffee wood waste, which reaches 338`086.000 kilos in the department of Huila. Starting from an experimental methodology, the coffee wood was prepared with its due drying, chip extraction, and sieving. A mixing was carried out at a temperature of 18 ºC with the following quantities: 16 g pulverized, 108 g polyester, 10 drops of cata specimens. 54 g polyester and 9 g pulverized were used for the tensile lyst in the flexural specimens. The results obtained from the laboratory and the use of the universal machine BESMAK, BMT ESeries; yielded a flexural value of 23,28 Mpa performed wi th the ASTM 790 standard and a tensile value of 19.71 Mpa with the ASTM D638 standard.Se obtuvo y caracterizó un material compuesto a partir de la matriz de poliéster y el refuerzo con pulverizado de madera de café; motivado por una necesidad de aprovechar los desechos de madera de café, que llegan a los 338`086.000 kilos en el departamento del Huila. Partiendo de una metodología experimental, se preparó la madera de café con su debido secado, extracción de viruta, y tamizado. Se realizó un mezclado a una temperatura de 18 ºC con las siguientes cantidades 16 g pulverizado, 108 g poliéster , 10 gotas de catalizador en las probetas de flexión. se usó 54 g poliéster y 9 g pulverizado para las probetas de tracción . Los resultados obtenidos de laboratorio y el uso de máquina universal BESMAK, BMT Series; arrojaron un valor por flexión de 23, 28 Mpa realizado con la norma ASTM 790E-- 17. y a tracción un valor de 19,71 Mpa con la norma ASTM D638.spaAcceso abiertoCompuestoTracciónFlexiónpolvo de madera de caféObtención y caracterización de un material compuesto de matriz poliéster reforzado con pulverizado de madera de caféTrabajo de grado (Pregrado y/o Especialización)CompositeTensileFlexureCoffee wood powderinfo:eu-repo/semantics/openAccesshttp://purl.org/coar/access_right/c_abf2Abril, C. G. P. (2019). Caracterización de la fibra del pseudo tallo de plátano como refuerzo y desarrollo de un material compuesto para fabricación de tejas. 114.Bai, J. (Ed.). (2013). Front matter. En Advanced Fibre-Reinforced Polymer (FRP) Composites for Structural Applications (pp. i-iii). Woodhead Publishing. https://doi.org/10.1533/9780857098641.frontmatterCafé de Huila. (s. f.). Federación Nacional de Cafeteros Huila. Recuperado 9 de marzo de 2022, de https://huila.federaciondecafeteros.org/cafe-de-cauca/Cafe.docx. (s. f.). ¿Recuperado 9 de marzo de 2022, de https://view.officeapps.live.com/op/view.aspx?Carlone, P., Sorrentino, L., & Kent, R. M. (2018). 7.16 Process Control for Polymeric Composite Manufacture. En P. W. R. Beaumont & C. H. Zweben (Eds.), Comprehensive Composite Materials II (pp. 337-354). Elsevier. https://doi.org/10.1016/B978-0-12-803581-8.03926-6Cavalcanti, W. M., de Oliveira, L. S., Cangussu, L. B., Maziero, R., & de Castro, D. (2020). Produção, caracterização química e mecânica de compósitos a partir de resíduos de madeira da construção civil e resinas epóxi de óleos vegetais. 8.Chung, D. D. L. (2017a). 3 - Polymer-Matrix Composites: Structure and Processing. En D. D. L. Chung (Ed.), Carbon Composites (Second Edition) (pp. 161-217). Butterworth-Heinemann. https://doi.org/10.1016/B978-0-12-804459-9.00003-8Chung, D. D. L. (2017b). 4 - Polymer-Matrix Composites: Mechanical Properties and Thermal Performance. En D. D. L. Chung (Ed.), Carbon Composites (Second Edition) (pp. 218-255). Butterworth-Heinemann. https://doi.org/10.1016/B978-012-804459-9.00004-XComposites, N. (2016). Naval Composites. Naval Composites. https://www.navalcomposites.comD. (2013). Characterization and mapping of waste from coffee and eucalyptus production in Brazil for thermochemical conversion of energy via gasification. Renewable and Sustainable Energy Reviews, 21, 52-58. https://doi.org/10.1016/j.rser.2012.12.025Díaz, Y. (2015). (PDF) Estudio preliminar de un material compuesto de matriz termoplástica con adición particulada en caracterización. https://doi.org/10.13140/RG.2.2.10122.88004instname:Universidad Antonio Nariñoreponame:Repositorio Institucional UANrepourl:https://repositorio.uan.edu.co/